Submerged Arc Welding Wires
SAW Wires
Wires for Submerged Arc Welding
Chemical Composition
Technical Data
Chemical composition of All Weld Metal (Typical) WITH Base Metal SM490
Saw Wire Characteristic & Application:
“Swastik Weld” EL-8 (Classification : AWS A5, 17, EL-8/EL 12)
Download Product Details
Welding wire electrode, Cu coated alloy steel wire is used for submerged arc welding and electroslag welding of unalloyed and low alloy steels with impact requirements higher than those obtainable with mild steel wires. Generally used by Pipe manufacturers for welding API grade Line pipes upto X75. We can also supply this grade with very low Sulphur and Phosphorus as per customer requirement. Welding wire of diameters in the range from 2.0 to 5.0mm. Larges diameters are produced upon a beforehand made agreements.
“Swastik Weld” EM-12K (Classification : AWS A5, 17, EM12K)
Welding wire electrode, Cu coated in combination with flux is suitable for welding low carbon steels, low alloyed steels and for medium and increased strength steels (construction, boiler and shipbuilding steels). It is used for making butt welds and fillet welds in general purpose steel constructions, pressure vessels. It is also used for pad welding on railways. Welding wire of diameters in the range from 2.0 to 5.0mm. Larges diameters are produced upon a beforehand made agreements.
“Swastik Weld” EH14 (Classification : AWS A5.17, EH14)
Welding wire electrode, Cu coated in combination with flux having increased Mn alloying component, is suitable for welding low-carbon steels, low-alloyed steels, for welding medium and increased strength steels (constructions, boilers and shipbuilding steels). Welding wire of diameters in the range from 2.0 to 5.0mm. Larges diameters are produced upon a beforehand made agreements.
“Swastik Weld” EH10K (Classification : A5.17 EH10K, A5.23 EH10K)
Submerged arc welding wire for standard CMn structural steels. Typical applications include shipbuilding, pressure vessels and general construction. For CMn and mild steels with yield strength up to ~420MPa (60ksi).